STRUCTURE: Cr
SPECIFIC DENSITY: 1.13
WATER ABSORBTION RATE (%): 0.03
ELONGATION (%): 3
TENSILE STRENGTH (psi): 8800
COMPRESSION STRENGTH (psi): 8500
FLEXURAL STRENGTH (psi): 12100
FLEXURAL MODULUS (psi): 700000
IMPACT (IZOD ft. lbs/in): 2.2
HARDNESS: R110
FABRICATION
- BONDING: P
- ULTRASONIC WELDING: P
- MACHINING: P
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi:
- @ 264 psi: 260
UTILZATION TEMPERATURE (deg. F)
- min: -14
- max: 284
MELTING POINT (deg. F): 338
COEFFICIENT OF EXPANSION: 0.000023
ARC RESISTANCE: 130
DIELECTRIC STRENGTH (kV/mm): 24
TRANSPARENCY: O
UV RESISTANCE: P
CHEMICAL RESISTANCE
- ACIDS: P
- ALKALIS: E
- SOLVENTS: P