STRUCTURE: Cr
SPECIFIC DENSITY: 0.90
WATER ABSORBTION RATE (%): 0.01
ELONGATION (%): 200
TENSILE STRENGTH (psi): 4000
COMPRESSION STRENGTH (psi): 5800
FLEXURAL STRENGTH (psi): 6500
FLEXURAL MODULUS (psi): 135000
IMPACT (IZOD ft. lbs/in): 6
HARDNESS: R80
FABRICATION
- BONDING: P
- ULTRASONIC WELDING: P
- MACHINING: G
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 174
- @ 264 psi: 140
UTILZATION TEMPERATURE (deg. F)
- min: -22
- max: 248
MELTING POINT (deg. F): 320
COEFFICIENT OF EXPANSION: 0.000065
ARC RESISTANCE: 180
DIELECTRIC STRENGTH (kV/mm): 22
TRANSPARENCY: T
UV RESISTANCE: P
CHEMICAL RESISTANCE
- ACIDS: G
- ALKALIS: E
- SOLVENTS: G