STRUCTURE: Cr
SPECIFIC DENSITY: 1.50
WATER ABSORBTION RATE (%): 0.5
ELONGATION (%): 6
TENSILE STRENGTH (psi): 8700
COMPRESSION STRENGTH (psi): 13000
FLEXURAL STRENGTH (psi): 11000
FLEXURAL MODULUS (psi): 550000
IMPACT (IZOD ft. lbs/in): 0.5
HARDNESS: R118
FABRICATION
- BONDING: G
- ULTRASONIC WELDING: G
- MACHINING: P
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 480
- @ 264 psi: 400
UTILZATION TEMPERATURE (deg. F)
- min: -94
- max: 284
MELTING POINT (deg. F): 490
COEFFICIENT OF EXPANSION: 0.000022
ARC RESISTANCE: 120
DIELECTRIC STRENGTH (kV/mm): 18
TRANSPARENCY: O
UV RESISTANCE: G
CHEMICAL RESISTANCE
- ACIDS: P
- ALKALIS: P
- SOLVENTS: G