STRUCTURE: A
SPECIFIC DENSITY: 1.10
WATER ABSORBTION RATE (%): 0.2
ELONGATION (%): 20
TENSILE STRENGTH (psi): 7200
COMPRESSION STRENGTH (psi): 8700
FLEXURAL STRENGTH (psi): 10000
FLEXURAL MODULUS (psi): 290000
IMPACT (IZOD ft. lbs/in): 0.8
HARDNESS: R110
FABRICATION
- BONDING: E
- ULTRASONIC WELDING: E
- MACHINING: P
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 194
- @ 264 psi: 185
UTILZATION TEMPERATURE (deg. F)
- min: -40
- max: 180
MELTING POINT (deg. F): 212
COEFFICIENT OF EXPANSION: 0.000045
ARC RESISTANCE: 80
DIELECTRIC STRENGTH (kV/mm): 18
TRANSPARENCY: C
UV RESISTANCE: P
CHEMICAL RESISTANCE
- ACIDS: G
- ALKALIS: E
- SOLVENTS: P