STRUCTURE: Cr
SPECIFIC DENSITY: 0.95
WATER ABSORBTION RATE (%): 0.01
ELONGATION (%): 700
TENSILE STRENGTH (psi): 3700
COMPRESSION STRENGTH (psi): 2500
FLEXURAL STRENGTH (psi): 1500
FLEXURAL MODULUS (psi): 175000
IMPACT (IZOD ft. lbs/in): NB
HARDNESS: SD68
FABRICATION
- BONDING: P
- ULTRASONIC WELDING: P
- MACHINING: G
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 176
- @ 264 psi: 131
UTILZATION TEMPERATURE (deg. F)
- min: -180
- max: 250
MELTING POINT (deg. F): 266
COEFFICIENT OF EXPANSION: 0.00007
ARC RESISTANCE: 180
DIELECTRIC STRENGTH (kV/mm): 22
TRANSPARENCY: T
UV RESISTANCE: P
CHEMICAL RESISTANCE
- ACIDS: G
- ALKALIS: E
- SOLVENTS: E