STRUCTURE: A
SPECIFIC DENSITY: 1.22
WATER ABSORBTION RATE (%): 2
ELONGATION (%): 50
TENSILE STRENGTH (psi): 6000
COMPRESSION STRENGTH (psi): 8500
FLEXURAL STRENGTH (psi): 8500
FLEXURAL MODULUS (psi): 180000
IMPACT (IZOD ft. lbs/in): 1.5
HARDNESS: R80
FABRICATION
- BONDING: P
- ULTRASONIC WELDING: P
- MACHINING: P
DEFLECTION TEMPERATURE (deg. F)
- @ 66 psi: 194
- @ 264 psi: 167
UTILZATION TEMPERATURE (deg. F)
- min: -40
- max: 212
MELTING POINT (deg. F): 248
COEFFICIENT OF EXPANSION: 0.00007
ARC RESISTANCE: 180
DIELECTRIC STRENGTH (kV/mm): 13
TRANSPARENCY: C
UV RESISTANCE: G
CHEMICAL RESISTANCE
- ACIDS: P
- ALKALIS: P
- SOLVENTS: P